China Serving Bowl - 29.3x8.6cm - Base: 8cm - Moule pour Fusing

Please Read: The steep angle of the mould may result in an uneven slumping. Reposition the slumped piece and fire a second time. Use a very low slumping temperature with a long soak.This firing recommendation has been calculated for use with Bullseye glass. Whereas the most typical casting glasses are frit and billets, you can have great results using sheet glass, stringers, rods as well as prefabricated components.The chart shown below is also based on the assumption that you are using a top fired kiln, e.g. Paragon GL22, GL24, BVD Flat bed kilns etc. Following this recommended firing chart will lead to a smooth piece of glass with a glossy surface. The finished piece will shrink somewhat, depending on the amount of glass used. Some coldworking on the edges with a diamond pad may be necessary. By lowering the temperature to a sinter firing (approx. 720°C) the piece will shrink less and have a 'sugary' look similar to pâte-de-verre.